CHARACTERIZATION OF STRENGTH OF ALUMINUM (Al 6063-T6) AFTER CORROSION

DR. PRAMOD KUMAR DASH, G Ram Vishal, Vinod L, Mahendra M A, Prashant Manvi

Abstract


Aluminum are frequently used as light weight structure in various nautical design. One of them is the ship structure design where sever environment of saline water influences the damage of the structure and one among them is pitting. In this paper, an experimental verification of strength and impact of corrosion effect on Al-6063 – T6 aluminum was presented. The specimens were exposed to saline water for various duration like 500hrs, 750hrs and 1000 hrs and tensile strength and yield strength was examined. The low velocity impact like 1J, 2J and 3J were used to make the damage on the specimens. Further, specimen’s residual strength was examined. Also, the strength reduction was verified through a mathematical formulation developed on the basis of residual strength model. The environmental exposed specimen’s data are compared with without exposed specimens and influence of environments are scaled. The theoretical results are almost matched with experimental results only with a difference of 2% approximately All observed results are presented in tables and figures for compared.


Keywords


CHARACTERIZATION OF STRENGTH OF Al 6063-T6 AFTER CORROSION

Full Text:

PDF

References


W. B. Wan Nik, O. Sulaiman, A. Fadhli, and R. Rosliza, Corrosion behaviour of aluminum alloy in sea water, Jr. marine technology, Vol 12, 2010, pp 175- 180

Hongyan Ding, Guanghong Zhou, Zhendong Dai, Yunfeng Bu, and Tongyang Jiang, Corrosion wear behaviors of 2024Al in artificial rainwater and seawater at fretting contact,Jr. wear, Vol 267, 2009, 292-298

C.N. Panagopoulos , E.P.Georgiou, and A.G.Gavras, Corrosion and wear of 6082 aluminum alloy, Jr. trigology international, Vol 42, 2009, 886-889

R.M. Chlistovsky, P.J. Heffernan,and D.L. DuQuesnay, Corrosion-fatigue behaviour of 7075-T651 aluminum alloy subjected to periodic overloads, Jr. fatigue, Vol 29, 2007, pp. 1941-1949

Zaki Ahmad, and B.J. Abdul Aleem, Degradation of aluminum metal matrix composites in salt water and its control, Jr. materials and design, Vol 23, 2002, 173-180

Al.Th. Kermanidis, P.V. Petroyiannis,and Sp.G. Pantelakis, Fatigue and damage tolerance behaviour of corroded 2024 T351 aircraft aluminum alloy, Jr. applied fracture mechanics, Vol 43, 2005, 121-132

Kunigahalli L. Vasanth, Catherine R. Wong and Richard A. Hays, Stress Corrosion Cracking Initiation Study in Nickel Aluminum Bronze in ASTM Seawater and Water- Ammonia Solutions, pp 1-11

Hosni Ezuber, A. El-Houd, and F.El-Shawesh, A study on the corrosion behaviour of aluminum alloys in seawater, Vol 29, 2008,pp 801-805

Sp.G. Pantelakis , A.N. Chamos, and D. Setsika, Tolerable corrosion damage on aircraft aluminum structures: Local cladding patterns. Jr. applied fracture mechanics, Vol 30, 2012, pp1-10

Sp.G. Pantelakis , P.G. Daglaras, and Ch.Alk. Apostolopoulos, Tensile and energy density properties of 2024, 6013, 8090 and 2091 aircraft aluminum alloy after corrosion exposure, Jr.Applied fracture mechanics, Vol 33, 2000, pp. 117-134

DU Zhi-Ming, CHEN Gang, LIU Jun, and XIE Shui-sheng, Tensile properties of as- deformed 2A50 aluminum alloy in semi-solid state, Jr. Transactions of Nonferrous Metals, Vol.20, 2010, pp. 1597 – 1602

H.J. Liu , H. Fujii , M. Maeda, and K. Nogi, Tensile properties and fracture locations of friction-stir-welded joints of 2017-T351 aluminum alloy, Jr. Material processing technology, Vol. 142, 2003, pp.692-696

V. Massardier, R. Fougeres and Merle, Mechanical properties of aluminum-based metal matrix composites reinforced with α-alumina platelets ,Jr. De physique, Vol 3, 1993, pp. 703-708

M. Cholewa, and M. Dziuba-Kałuza, Analysis of structural properties of aluminum skeleton castings regarding the crystallization kinetics, Jr. materials science and engineering, Vol 38, 2009, pp 93-102

H. Kamoutsi, G.N. Haidemenopoulos, V. Bontozoglou, and S. Pantelakis , Corrosion- induced hydrogen embrittlement in aluminum alloy 2024, Jr. corrosion science, Vol48, 2006, pp 1200- 1224

D.G. Harlow and R.P.Wei, A probability model for the growth of corrosion pits in aluminum alloys induced by constituent particles, Jr. engineering fracture mechanics, Vol 59, 1998, pp 305-325

A.N. Shuaib, Mechanical properties of Al_2.5 Mg_0.1 Mn_Si_Cr_Fe Alloys, Jr. materials and design, Vol 23, 2002, pp 181-187

D.L. DuQuesnay, P.R. Underhill, and H.J. Britt, Fatigue crack growth from corrosion damage in 7075-T6511 aluminum alloy under aircraft loading, Jr. fatigue, Vol 25, 2003, 373-377

Sp.G Pantelakis, Al.Th. Kermanidis and P.G.Daglaras, Crack growth analysis code for assessing fatigue life of 2219 T851 aluminum specimens under aircraft structure service spectra, Jr. applied fracture mechanics, Vol 28, 1997, pp 1-12

T.S. Srivatsan, D. Kolar, and P. Magnusen, The cyclic fatigue and final fracture behavior of aluminum alloy 2524, Jr. materials and design, Vol 23,2002,pp 129-139

R.A. Siddiqui, S.A. Abdul-Wahab ,and T. Pervez, Effect of aging time and aging temperature on fatigue and fracture behavior of 6063 aluminum alloy under seawater influence, Jr. materials and design, Vol 29, 2008, pp 70 -79

C.N.Duong. C.C.Chen and J .Yu, An energy approach ti the link up of multiple cracks in thin aluminum alloy sheets, Jr. applied fracture mechnanics, Vol 35, 2001, 11-127

K.S. Tan, J.A. Wharton, and R.J.K. Wood, Solid particle erosion–corrosion behaviour of a novel HVOF nickel aluminum bronze coating for marine applications—correlation between mass loss and electrochemical measurements, Jr. wear, Vol 258, 2005


Refbacks

  • There are currently no refbacks.


Copyright (c) 2022 Journal of Experimental & Applied Mechanics